CELSTRAN TPU-GF60-01-US | TPU | Glass Reinforced
 
Description
60% long strand glass fiber reinforced thermoplastic polyurethane
 
Other Processing
Injection Molding
Celstran can be processed on a standard injection molding unit. A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.
 
Melt Temp:260-265℃.
Mold Temp:70-75℃.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1760 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 18700 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 240 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.75 % ISO 527-2/1A
Flexural modulus (23℃) 18300 MPa ISO 178
Flexural strength (23℃) 420 MPa ISO 178
Charpy notched impact strength @ 23℃ 66 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 102 ISO 75-1/-2
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.05%
 
CELSTRAN TPU should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible
 
Drying time (h):4
Drying temperature (℃):80 - 80