LNP™ STAT-KON™ Compound PU TE002
 
Also known as:LNP™ Stat-kon™ Compound TC-1002 Product reorder name:TE002
LNP* Stat-kon* TE002 is a compound based on Polyurethane resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
 
Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 530 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 490 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 19.2 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 22.8 % ASTM D 638
Tensile Modulus,50mm/min 13300 kgf/cm² ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 11800 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 50 MPa ISO 527
Tensile Stress,break,5mm/min 49 MPa ISO 527
Tensile Strain,yield,5mm/min 15.7 % ISO 527
Tensile Strain,break,5mm/min 19.8 % ISO 527
Tensile Modulus,1mm/min 1580 MPa ISO 527
Flexural Stress 51 MPa ISO 178
Flexural Modulus,2mm/min 1660 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 172 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 48 cm-kgf/cm ASTM D 256
Multiaxial Impact 153 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 234 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 128 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 37 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 141 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 82 ASTM D 648
CTE,-30℃ to 30℃,flow 1.00E-06 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 1.60E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 175 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 88 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.27 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.46 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1-0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.2-0.4 % ASTM D 955
Density 1.27 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.6 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 5.E+00-8.E+00 Ohm ASTM D 257
Source GMD,last updated:2008/10/22
Parameter Injection Molding Value Unit
Drying Temperature 95-105
Drying Time 2 hrs
Maximum Moisture Content 0.03 %
Melt Temperature 210
Nozzle Temperature 205-225
Front-Zone 3 Temperature 200-220
Middle-Zone 2 Temperature 195-215
Rear-Zone 1 Temperature 195-210
Mold Temperature 15-45
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Shot to Cylinder Size 40-80 %
Source GMD,last updated:2008/10/22