LNP STAT-KON PU TD000

添加时间:2013-02-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP™ STAT-KON™ Compound PU TD000
 
Also known as:LNP™ Stat-kon™ Compound T Product reorder name:TD000
LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.
 
Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,break 260 kgf/cm² ASTM D 638
Tensile Stress,yld,Type I,50mm/min 260 kgf/cm² ASTM D 638
Tensile Strain,break 160 % ASTM D 638
Tensile Strain,yld,Type I,50mm/min 160 % ASTM D 638
Tensile Modulus,50mm/min 1800 kgf/cm² ASTM D 638
Flexural Stress 70 kgf/cm² ASTM D 790
Flexural Modulus 3700 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 24 MPa ISO 527
Tensile Stress,break,5mm/min 24 MPa ISO 527
Tensile Strain,yield,5mm/min 140 % ISO 527
Tensile Strain,break,5mm/min 140 % ISO 527
Tensile Modulus,1mm/min 300 MPa ISO 527
Flexural Stress 16 MPa ISO 178
Flexural Modulus,2mm/min 350 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 102 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 80 cm-kgf/cm ASTM D 256
Multiaxial Impact 565 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 516 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 87 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 78 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 70 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 47 ASTM D 648
CTE,-30℃ to 30℃,flow 1.20E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 1.40E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 69 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 48 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.26 - ASTM D 792
Density 1.26 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.5 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1-3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1-3 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.79 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+04-1.E+06 Ohm ASTM D 257
Source GMD,last updated:2011/06/28
Parameter Injection Molding Value Unit
Drying Temperature 80-95
Drying Time 2-4 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.1 %
Melt Temperature 220-260
Nozzle Temperature 220-260
Front-Zone 3 Temperature 215-240
Middle-Zone 2 Temperature 205-225
Rear-Zone 1 Temperature 190-210
Mold Temperature 50-70
Back Pressure 0.3-0.7 MPa
Screw Speed 30-60 rpm
Shot to Cylinder Size 50-70 %
Vent Depth 0.038-0.051 mm
Source GMD,last updated:2011/06/28