LNP THERMOCOMP TPE WX05456

添加时间:2013-02-26  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

LNP™ THERMOCOMP™ Compound TPE WX05456


Also known as:LNP™ Thermocomp™ Compound 9760 Product reorder name:WX05456
LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral.


Property
TYPICAL PROPERTIES(1)

MECHANICAL Value Unit Standard
Tensile Stress,break 490 kgf/cm² ASTM D 638
Tensile Strain,break 1.8 % ASTM D 638
Tensile Modulus,50mm/min 43000 kgf/cm² ASTM D 638
Flexural Stress 920 kgf/cm² ASTM D 790
Flexural Modulus 44700 kgf/cm² ASTM D 790
Tensile Stress,break 47 MPa ISO 527
Tensile Strain,break 1.4 % ISO 527
Tensile Modulus,1mm/min 4650 MPa ISO 527
Flexural Stress 88 MPa ISO 178
Flexural Modulus 4200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 20 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 2 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 73 cm-kgf ASTM D 3763
Multiaxial Impact 6 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 15 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 2 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 171 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 71 ASTM D 648
CTE,-40℃ to 40℃,flow 5.81E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 6.67E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 5.81E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 6.68E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 163 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 82 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.546 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.05 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1.5 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 1.47 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 1.51 % ISO 294
Density 1.54 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 1.5 mm UL 94 by SABIC-IP
Source GMD,last updated:2004/10/01
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-275
Front-Zone 3 Temperature 265-275
Middle-Zone 2 Temperature 250-260
Rear-Zone 1 Temperature 230-245
Mold Temperature 80-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/10/01