PPS PPS-GF50-01-US 含50%长玻璃纤维

添加时间:2013-05-17  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS PPS-GF50-01-US
 
CELSTRAN® PPS-GF50-01 AD3002 BLACK
CELSTRAN® PPS-GF50-01 AF3001 NATURAL
 
CELSTRAN PPS-GF50-01-US | PPS | Glass Reinforced
 
Description
50% long strand glass fiber reinforced polyphenylene sulfide
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1720 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 18200 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 150 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.04 % ISO 527-2/1A
Flexural modulus (23℃) 17300 MPa ISO 178
Flexural strength (23℃) 265 MPa ISO 178
Charpy notched impact strength @ 23℃ 23 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 282 ISO 75-1/-2
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3-4
Drying temperature (℃):130-140