PPS MT9205C4
 
FORTRON® MT® 9205C4 SD3039 BLACK
FORTRON® MT® 9205C4 SF3001 NATURAL
 
FORTRON MT9205C4 | PPS | Medical Technology
 
Description
Fortron MT9205C4 is an unfilled grade with a low melt viscosity used for custom compounding and extrusion. It demonstrates an excellent chemical resistance and thermal stability. Components made with this base resin may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron MT9205C4 is in compliance with ISO 10993, USP Class VI, and is included in the Fortron Drug and Device Master Files at the FDA. It complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1350 kg/m³ ISO 1183
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 4000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 65 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2 % ISO 527-2/1A
Flexural modulus (23℃) 3900 MPa ISO 178
Flexural strength (23℃) 120 MPa ISO 178
Notched impact strength (Izod) @ 23℃ 2 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 115 ISO 75-1/-2
DTUL @ 8.0 MPa 95 ISO 75-1/-2
Eiec Electrical properties Value Unit Test Standard
Relative permittivity - 10kHz 3.3 - IEC 60250
Relative permittivity - 1 MHz 3.2 - IEC 60250
Volume resistivity 1E13 Ohm*m IEC 60093
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):110 - 120