PPS MT9115L0 DW
 
FORTRON® MT® 9115L0 SD3039 BLACK(DW)
 
FORTRON MT9115L0 DW | PPS | Specialty
 
Description
Fortron® MT9115L0 DW is a 15% fiberglass-reinforced grade of polyphenylene sulfide with high melt strength suitable for blow molding and extrusion applications.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1440 kg/m³ ISO 1183
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 7700 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 120 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2 % ISO 527-2/1A
Flexural modulus (23℃) 7500 MPa ISO 178
Flexural strength (23℃) 200 MPa ISO 178
Charpy impact strength @ 23℃ 32 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 5 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 5.2 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 220 ISO 75-1/-2
DTUL @ 8.0 MPa 115 ISO 75-1/-2
Elec Electrical properties Value Unit Test Standard
Surface resistivity >1E15 Ohm IEC 60093
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):130 - 140