PPS 6341L4 玻璃纤维40%增强

添加时间:2013-05-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 6341L4
 
FORTRON® 6341L4 SD3002 BLACK
FORTRON® 6341L4 SF3001 NATURAL
 
FORTRON 6341L4 | PPS | Specialty
 
Description
Fortron 6341L4 is a tribological-modified Fortron®-PPS containing 40% glass fibre. Fortron 6341L4 comprises the same mechanical properties like Fortron 1342L4, but with a different tribological adjustment.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1700 kg/m³ ISO 1183
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 14400 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 165 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.6 % ISO 527-2/1A
Flexural modulus (23℃) 13700 MPa ISO 178
Flexural stress @ break 245 MPa ISO 178
Charpy impact strength @ 23℃ 40 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 8 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 8 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 270 ISO 75-1/-2
DTUL @ 8.0 MPa 215 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.2 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.4 E-4/℃ ISO 11359-2
 
Processing
Pre Drying
Drying time (h):3 - 4
Drying temperature (℃):130 - 140