PPS 6165A4 含65%玻璃矿物填充

添加时间:2013-05-21  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 6165A4
 
FORTRON® 6165 SD3002 BLACK
FORTRON® 6165 SY3004 BROWN
FORTRON® 6165A4 SD3002 BLACK
FORTRON® 6165A4 SF3001 NATURAL
FORTRON® 6165A4 SY3004 BROWN
FORTRON® 6165A4-W SF3001 NATURAL
 
FORTRON 6165A4 | PPS | Mineral / Glass Reinforced
 
Description
Fortron 6165A4 offers a unique balance of properties based on a high mineral and glass reinforced composition. The heat resistance under load bearing conditions is excellent for this product. As with all Fortron grades this product is inherently flame-retardant. Applications include electronic components (i.e. lamp houses, connection parts and sockets) and components in industry (i.e. pumps and pistons).
 
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
 
Melt temperature 320-340 degC
Mold wall temperature  at least 140 degC
 
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1950 kg/m³ ISO 1183
Mold shrinkage - parallel 0.2 - 0.6 % ISO 294-4
Mold shrinkage - normal 0.3 - 0.7 % ISO 294-4
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 19000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 130 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.2 % ISO 527-2/1A
Flexural modulus (23℃) 18800 MPa ISO 178
Flexural stress @ break 210 MPa ISO 178
Charpy impact strength @ 23℃ 20 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 20 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 7 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 7 kJ/m² ISO 179/1eA
Unnotched impact str (Izod) @ 23℃ 20 kJ/m² ISO 180/1U
Notched impact strength (Izod) @ 23℃ 6 kJ/m² ISO 180/1A
Notched impact strength (Izod) @-30℃ 6 kJ/m² ISO 180/1A
Rockwell hardness 100 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 270 ISO 75-1/-2
DTUL @ 8.0 MPa 215 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.19 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.24 E-4/℃ ISO 11359-2
Limiting oxygen index (LOI) 53 % ISO 4589
Flammability @1.6mm nom. thickn. V-0 class UL94
thickness tested (1.6) 1.5 mm UL94
Flammability at thickness h V-0 class UL94
thickness tested (h) 0.75 mm UL94
Flammability 5V at thickness h 5VA class UL94
thickness tested (5V) 3 mm UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 10kHz 5.4 - IEC 60250
Relative permittivity - 1 MHz 5.6 - IEC 60250
Dissipation factor - 10kHz 10 E-4 IEC 60250
Dissipation factor - 1 MHz 20 E-4 IEC 60250
Volume resistivity >1E15 Ohm*m IEC 60093
Surface resistivity >1E15 Ohm IEC 60093
Electric strength 25 kV/mm IEC 60243-1
Comparative tracking index CTI 175 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310 - 340 ISO 294
Injection molding mold temperature 135 - 160 ISO 294
Rheo Rheological Calculation properties Value Unit Test Standard
Specific heat capacity of melt 1600 J/(kg K) Internal
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):130 - 140