PPS 6162A7 含玻璃矿物填充

添加时间:2013-05-21  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 6162A7
 
FORTRON® 6162A7 SD3002 BLACK
 
FORTRON 6162A7 | PPS | Mineral / Glass Reinforced
 
Description
Fortron 6162A7 is a mineral/glass reinforced grade for applications requiring the highest flow.
 
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
 
Melt temperature 320-340 degC
Mold wall temperature  at least 140 degC
 
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1920 kg/m³ ISO 1183
Mold shrinkage - parallel 0.1-0.3 % ISO 294-4
Mold shrinkage - normal 0.4-0.8 % ISO 294-4
Water absorption (23℃-sat) 0.017 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 15400 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 115 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.3 % ISO 527-2/1A
Flexural modulus (23℃) 14500 MPa ISO 178
Flexural strength (23℃) 185 MPa ISO 178
Flexural strain @ break 1.5 % ISO 178
Charpy impact strength @ 23℃ 16 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 28.2 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 4.5 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 7.7 kJ/m² ISO 179/1eA
Unnotched impact str (Izod) @ 23℃ 18 kJ/m² ISO 180/1U
Notched impact strength (Izod) @ 23℃ 6 kJ/m² ISO 180/1A
Notched impact strength (Izod) @-30℃ 8.9 kJ/m² ISO 180/1A
Rockwell hardness 100 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 270 ISO 75-1/-2
DTUL @ 8.0 MPa 215 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.19 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.34 E-4/℃ ISO 11359-2
Flammability @1.6mm nom. thickn. V-0 class UL94
thickness tested (1.6) 1.5 mm UL94
Flammability at thickness h V-0 class UL94
thickness tested (h) 0.8 mm UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 10kHz 5.84 - IEC 60250
Relative permittivity - 1 MHz 5.68 - IEC 60250
Dissipation factor - 10kHz 80 E-4 IEC 60250
Dissipation factor - 1 MHz 10 E-4 IEC 60250
Comparative tracking index CTI 225 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310 - 340 ISO 294
Injection molding mold temperature 135 - 160 ISO 294
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):130 - 140