PPS 6160B4 含60%玻璃矿物填充

添加时间:2013-05-21  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 6160B4
 
FORTRON® 6160B4 SD3002 BLACK
 
FORTRON 6160B4 | PPS | Mineral / Glass Reinforced
 
Description
Fortron 6160B4 has excellent heat and chemical resistance as well as good electrical properties. This product is inherently flame-retardant and offers high hardness and rigidity. 6160B4 has demonstrated excellent performance in hot runner systems and superior contact corrosion resistance. Applications include electronic components (i.e. molded in lead frames, contacts or pins).
 
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
 
Melt temperature 320-340 degC
Mold wall temperature  at least 140 degC
 
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1900 kg/m³ ISO 1183
Mold shrinkage - parallel 0.2 - 0.6 % ISO 294-4
Mold shrinkage - normal 0.3 - 0.7 % ISO 294-4
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 17300 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 145 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1 % ISO 527-2/1A
Flexural modulus (23℃) 16700 MPa ISO 178
Flexural stress @ break 220 MPa ISO 178
Charpy impact strength @ 23℃ 27 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 27 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 7 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 7 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 7 kJ/m² ISO 180/1A
Notched impact strength (Izod) @-30℃ 7 kJ/m² ISO 180/1A
Rockwell hardness 100 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 270 ISO 75-1/-2
DTUL @ 8.0 MPa 220 ISO 75-1/-2
Flammability @1.6mm nom. thickn. V-0 class UL94
thickness tested (1.6) 1.5 mm UL94
Flammability at thickness h V-0 class UL94
thickness tested (h) 0.81 mm UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 10kHz 4.9 - IEC 60250
Relative permittivity - 1 MHz 4.9 - IEC 60250
Dissipation factor - 10kHz 5 E-4 IEC 60250
Dissipation factor - 1 MHz 10 E-4 IEC 60250
Volume resistivity >1E13 Ohm*m IEC 60093
Surface resistivity >1E15 Ohm IEC 60093
Electric strength 26 kV/mm IEC 60243-1
Comparative tracking index CTI 175 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310 - 340 ISO 294
Injection molding mold temperature 135 - 160 ISO 294
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):130 - 140