FORTRON 6150T6 | PPS | Specialty
 
Description
Fortron 6150T6 is a 50% glass-fiber reinforced and mineral-filled grade with improved impact and heat shock resistance.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1750 kg/m³ ISO 1183
Mold shrinkage - parallel 0.1 - 0.2 % ISO 294-4
Mold shrinkage - normal 0.4 - 0.5 % ISO 294-4
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 13000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 140 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.6 % ISO 527-2/1A
Flexural modulus (23℃) 12300 MPa ISO 178
Flexural stress @ break 200 MPa ISO 178
Charpy impact strength @ 23℃ 40 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 8 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 270 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.15 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.43 E-4/℃ ISO 11359-2
Elec Electrical properties Value Unit Test Standard
Volume resistivity >1E13 Ohm*m IEC 60093
Comparative tracking index CTI 175 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310 - 340 ISO 294
Injection molding mold temperature 135 - 160 ISO 294
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):130 - 140