PPS 4184L6 含53%玻璃/矿物, 流动性良好

添加时间:2013-05-21  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 4184L6
 
FORTRON® 4184L6 SC3010 GRAY
FORTRON® 4184L6 SD3002 BLACK
FORTRON® 4184L6 SF3001 NATURAL
FORTRON® 4184L6 SY3004 BROWN
 
FORTRON 4184L6 | PPS | Mineral / Glass Reinforced
 
Description
Fortron 4184L6 is an easier flow version of Fortron 4184L4. It offers similar characteristics to the 4184L4. This grade is especially used for thin walled parts requiring long flow lengths, stiffness and dimensional control. Applications made of this grade are typically electronic components.
 
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
 
Melt temperature 320-340 degC
Mold wall temperature  at least 140 degC
 
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1800 kg/m³ ISO 1183
Mold shrinkage - parallel 0.3 - 0.6 % ISO 294-4
Mold shrinkage - normal 0.4 - 0.7 % ISO 294-4
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 16600 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 165 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.4 % ISO 527-2/1A
Flexural modulus (23℃) 16200 MPa ISO 178
Flexural stress @ break 250 MPa ISO 178
Charpy impact strength @ 23℃ 29 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 29 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 7 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 7 kJ/m² ISO 179/1eA
Unnotched impact str (Izod) @ 23℃ 27 kJ/m² ISO 180/1U
Notched impact strength (Izod) @ 23℃ 7 kJ/m² ISO 180/1A
Notched impact strength (Izod) @-30℃ 7 kJ/m² ISO 180/1A
Rockwell hardness 100 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 270 ISO 75-1/-2
DTUL @ 8.0 MPa 215 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.24 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.32 E-4/℃ ISO 11359-2
Flammability @1.6mm nom. thickn. V-0 class UL94
thickness tested (1.6) 1.5 mm UL94
Flammability at thickness h V-0 class UL94
thickness tested (h) 0.75 mm UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 10kHz 4.7 - IEC 60250
Relative permittivity - 1 MHz 4.7 - IEC 60250
Dissipation factor - 10kHz 8 E-4 IEC 60250
Dissipation factor - 1 MHz 20 E-4 IEC 60250
Volume resistivity >1E13 Ohm*m IEC 60093
Surface resistivity >1E15 Ohm IEC 60093
Electric strength 27 kV/mm IEC 60243-1
Comparative tracking index CTI 150 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310 - 340 ISO 294
Injection molding mold temperature 135 - 160 ISO 294
Rheo Rheological Calculation properties Value Unit Test Standard
Specific heat capacity of melt 1500 J/(kg K) Internal
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3 - 4
Drying temperature (℃):130 - 140