PPS 1200L1 未填充,粘度高

添加时间:2013-05-21  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 1200L1
 
FORTRON® 1200L1 SF3001 NATURAL
 
FORTRON 1200L1 | PPS | Specialty
 
Description
Fortron 1200L1 is an unfilled grade for extrusion applications, which has a high melt viscosity and tensile elongation. The recommended processing conditions are identical to those of our standard unfilled grades.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1340 kg/m³ ISO 1183
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 4000 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 3 % ISO 527-2/1A
Tensile stress at break (50mm/min) 88 MPa ISO 527-2/1A
Tensile strain at break (50mm/min) 15 % ISO 527-2/1A
Flexural modulus (23℃) 4100 MPa ISO 178
Flexural strength (23℃) 141 MPa ISO 178
Charpy impact strength @ 23℃ 200 kJ/m² ISO 179/1eU
Rockwell hardness 93 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 275 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
Coeff.of linear therm. expansion (parallel) 0.4 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.42 E-4/℃ ISO 11359-2
Elec Electrical properties Value Unit Test Standard
Electric strength 30 kV/mm IEC 60243-1
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
Drying time (h):3-4 hours
Drying temperature (℃):110-120