PPS 1131L4 ITT 含30%玻璃纤维增强

添加时间:2013-05-20  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 1131L4 ITT
 
FORTRON 1131L4 ITT | PPS | Glass Reinforced
PPS 1131L4 ITT 是一个含30%玻璃纤维增强的聚苯硫醚材料。
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1560 kg/m³ ISO 1183
Mold shrinkage - parallel 0.3-0.7 % ISO 294-4
Mold shrinkage - normal 0.5-0.8 % ISO 294-4
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 12200 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 165 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.9 % ISO 527-2/1A
Flexural modulus (23℃) 12000 MPa ISO 178
Flexural stress @ break 255 MPa ISO 178
Charpy impact strength @ 23℃ 42 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 42 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 8 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 8 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 8 kJ/m² ISO 180/1A
Notched impact strength (Izod) @-30℃ 8 kJ/m² ISO 180/1A
Rockwell hardness 100 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 265 ISO 75-1/-2
DTUL @ 8.0 MPa 205 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.29 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.62 E-4/℃ ISO 11359-2
Flammability @1.6mm nom. thickn. V-0 class UL94
thickness tested (1.6) 1.5 mm UL94
Flammability at thickness h V-0 class UL94
thickness tested (h) 0.38 mm UL94
Elec Electrical properties Value Unit Test Standard
Volume resistivity >1E13 Ohm*m IEC 60093
Surface resistivity >1E15 Ohm IEC 60093
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310-340 ISO 294
Injection molding mold temperature 135-160 ISO 294
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3-4
Drying temperature (℃):130-140
 