PPS 1130L0 含30玻纤增强,挤出级

添加时间:2013-05-20  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 1130L0
 
FORTRON® 1130L0 SD3002 BLACK
FORTRON® 1130L0 SF3001 NATURAL
 
FORTRON 1130L0 | PPS | Glass Reinforced
 
Description
Fortron 1130L0 is a 30% glass-reinforced extrusion grade. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. 1130L0 is used to produce rods and slabs.
 
ISO Data Mechanical properties Value Unit Test Standard
Mech Tensile modulus (1mm/min) 11000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 160 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2 % ISO 527-2/1A
Flexural modulus (23℃) 10400 MPa ISO 178
Flexural strength (23℃) 255 MPa ISO 178
Charpy notched impact strength @ 23℃ 10 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 10 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 9.5 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 280 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 90 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 255 ISO 75-1/-2
Flammability at thickness h V-0 class UL94
thickness tested (h) 0.38 mm UL94
Elec Electrical properties Value Unit Test Standard
Volume resistivity 1E+16 Ohm*m IEC 60093
Surface resistivity 1E+16 Ohm IEC 60093
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 310-340 ISO 294
Injection molding mold temperature 135-160 ISO 294
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3-4
Drying temperature (℃):130-140
 