PPS 1115T1 含15%玻纤增强,吹塑级

添加时间:2013-05-18  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 1115T1
 
FORTRON 1115T1 | PPS | Specialty
 
Description
Fortron® 1115T1 is a 15% fiberglass-reinforced grade of polyphenylene sulfide suitable for blow molding applications.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1410 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 6700 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 115 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.5 % ISO 527-2/1A
Flexural modulus (23℃) 6500 MPa ISO 178
Flexural strength (23℃) 190 MPa ISO 178
Flexural strain @ break 2.9 % ISO 178
Charpy impact strength @ 23℃ 39 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 6.2 kJ/m² ISO 179/1eA
Unnotched impact str (Izod) @ 23℃ 34 kJ/m² ISO 180/1U
Notched impact strength (Izod) @ 23℃ 7 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 210 ISO 75-1/-2
DTUL @ 8.0 MPa 104 ISO 75-1/-2
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3-4
Drying temperature (℃):80-100
 