PPS 1115L0 含15%玻璃纤维强化

添加时间:2013-05-18  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
PPS 1115L0
 
FORTRON® 1115L0 BLACK
FORTRON® 1115L0 SD3002 BLACK
 
FORTRON 1115L0 | PPS | Specialty
 
Description
Fortron® 1115L0 is a 15% fiberglass-reinforced grade of polyphenylene sulfide with high melt strength suitable for blow molding and extrusion applications.
The recommended processing conditions are similar to those of our standard grades, except drying conditions are somewhat milder at 80 to 100 C for 3-4 hours.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1440 kg/m³ ISO 1183
Water absorption (23℃-sat) 0.02 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 7700 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 120 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2 % ISO 527-2/1A
Flexural modulus (23℃) 7500 MPa ISO 178
Flexural strength (23℃) 200 MPa ISO 178
Charpy impact strength @ 23℃ 32 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 5 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 5.2 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 220 ISO 75-1/-2
DTUL @ 8.0 MPa 115 ISO 75-1/-2
Elec Electrical properties Value Unit Test Standard
Surface resistivity >1E15 Ohm IEC 60093
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
 
Drying time (h):3-4
Drying temperature (℃):110-120
 