PP PP-GF30-04 含30%长玻纤增强,热稳定

添加时间:2013-06-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
celstran PP PP-GF30-04
 
COMPEL PP-GF30-04 | PP | Glass Reinforced
 
Description
Heat Stabilized Polypropylene reinforced with 30% long glass fiber
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1120 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 7200 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 95 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.3 % ISO 527-2/1A
Flexural modulus (23℃) 7000 MPa ISO 178
Charpy impact strength @ 23℃ 48 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 44 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 18 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 20 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 148 ISO 75-1/-2
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.2%
 
It is normally not necessary to dry CELSTRAN PP. However, should there be surface moisture (condensate) on the molding compound as a result of incorrect storage, drying is required.
 
The product can then be stored in standard conditions until processed.
 
Drying time (h):2.00
Drying temperature (℃):90 - 100
 