PP PP-GF30-04 含30%长玻纤,高耐热

添加时间:2013-06-19  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
celstran PP PP-GF30-04
 
CELSTRAN PP-GF30-04 | PP | Glass Reinforced
 
Description
Material code according to ISO 1043-1: PP
 
Heat stabilized polypropylene reinforced with 30 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
 
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
 
The very isotropic shrinkage in the molded parts minimizes the warpage.
 
Complex parts can be manufactured with high reproducibility by injection molding.
 
Application field: Functionial/structural parts for automotive
 
ISO Data Mechanical properties Value Unit Test Standard
Mech Tensile modulus (1mm/min) 6600 MPa ISO 527-2/1A
Tensile modulus (80℃) 4400 MPa ISO 527-2/1A
Tensile strength (80℃) 52 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 95 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.3 % ISO 527-2/1A
Elongation at break (80℃) 2.9 % ISO 527-2/1A
Flexural modulus (23℃) 7000 MPa ISO 178
Flexural modulus (80℃) 4800 MPa ISO 178
Flexural strength (23℃) 160 MPa ISO 178
Flexural strength (80℃) 95 MPa ISO 178
Charpy impact strength @ 23℃ 48 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 44 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 18 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 20 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 148 ISO 75-1/-2
DTUL @ 8.0 MPa 122 ISO 75-1/-2
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.2%
 
It is normally not necessary to dry CELSTRAN PP. However, should there be surface moisture (condensate) on the molding compound as a result of incorrect storage, drying is required.
 
The product can then be stored in standard conditions until processed.
 
Drying time (h):4
Drying temperature (℃):90 - 100
 