添加时间:2013-06-18  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
celstran PP PP-GF25-0403 P10/10
 
CELSTRAN® PP-GF25-0403P10/10
 
CELSTRAN PP-GF25-0403 P10/10 | PP | Glass Reinforced
 
Description
Material code according to ISO 1043-1: PP
 
Polypropylene reinforced with 25weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
 
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
 
The very isotropic shrinkage in the molded parts minimizes the warpage.
 
Complex parts can be manufactured with high reproducibility by injection molding.
 
Application field: Functionial/structural parts for automotive
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1090 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 6400 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 105 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.3 % ISO 527-2/1A
Charpy impact strength @ 23℃ 50 kJ/m² ISO 179/1eU
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 166 ISO 11357-1,-2,-3
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.2%
 
It is normally not necessary to dry CELSTRAN PP. However, should there be surface moisture (condensate) on the molding compound as a result of incorrect storage, drying is required. A circulating air drying cabinet can be used for this purpose if the gran
 
The product can then be stored in standard conditions until processed.
 
Drying time (h):4
Drying temperature (℃):90 - 100
 