hostaform pom TF-10XAP
 
HOSTAFORM® TF-10 XAP® 14 BLACK
HOSTAFORM® TF-10 XAP® NATURAL
 
HOSTAFORM TF-10XAP® | POM | Impact Modified
 
Description
Hostaform® acetal copolymer TF-10 XAP® is low emission, improved flow, impact modified grade providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performance with improved impact in many applications.
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1380 kg/m³ ISO 1183
Melt volume rate (MVR) 13 cm³/10min ISO 1133
MVR test temperature 190 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 2.1 % ISO 294-4
Mold shrinkage - normal 1.9 % ISO 294-4
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 1750 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 49 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 13 % ISO 527-2/1A
Flexural modulus (23℃) 1700 MPa ISO 178
Charpy notched impact strength @ 23℃ 10 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 7 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 165 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 75 ISO 75-1/-2
DTUL @ 0.45 MPa 139 ISO 75-1/-2
 
Processing
Pre Drying
Drying is recommended.
 
Drying time (h):3
Drying temperature (℃):80 - 100