HOSTAFORM S 9363 | POM | Impact Modified
 
Description
Preliminary Data Sheet
Hostaform® acetal copolymer grade S 9363 is an impact modified grade for demanding applications. Hostaform® S 9363 provides good impact strength while improving modulus and weld line strength over standard impact modified grades such as Hostaform® S 9064.
 
Chemical abbreviation according to ISO 1043-1: POM-HI
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1380 kg/m³ ISO 1183
Melt volume rate (MVR) 5.5 cm³/10min ISO 1133
MVR test temperature 190 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 1.8 % ISO 294-4
Mold shrinkage - normal 1.6 % ISO 294-4
Water absorption (23℃-sat) 0.8 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 2000 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 50 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 12 % ISO 527-2/1A
Flexural modulus (23℃) 2000 MPa ISO 178
Charpy impact strength @ 23℃ NB kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ NB kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 13 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 8 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 166 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 84 ISO 75-1/-2
DTUL @ 0.45 MPa 148 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1.1 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 1.1 E-4/℃ ISO 11359-2
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988-2 - Internal
 
Processing
Pre Drying
Drying is not normally required. If material has contacted moisture through improper storage and handling or through regrind use, dry to prevent splay and odor problems.
 
Drying time (h):3
Drying temperature (℃):80 - 100