添加时间:2013-06-14  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

hostaform pom EC140XF

HOSTAFORM® EC140XF CD3068 BLACK

 
HOSTAFORM EC140XF | POM | Specialty
 
Description
Hostaform® EC140XF is a conductive ESD grade of acetal copolymer for applications requiring dissipation of static build-up. EC140XF has an improved resistance to aggressive fuel blends.
 
Other Processing
Injection Molding
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the Hostaform® material.
 
Melt Temperature: Preferred range 182-199℃ (360-390℉). Melt temperature should never exceed 230℃ (450℉).Mold Surface Temperature: Preferred range 82-93℃ (180-200℉) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120℃ (250℉) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65℃/150℉) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25℃ (80℉). In general, mold surface temperatures lower than 82℃ (180℉) may produce a hazy surface or a surface with flow lines, pits and other included defects.
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1420 kg/m³ ISO 1183
Melt volume rate (MVR) 4 cm³/10min ISO 1133
MVR test temperature 190 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 2.1 % ISO 294-4
Mold shrinkage - normal 1.9 % ISO 294-4
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 2700 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 53 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 4.7 % ISO 527-2/1A
Tensile strain at break (50mm/min) 12 % ISO 527-2/1A
Flexural modulus (23℃) 2650 MPa ISO 178
Charpy impact strength @ 23℃ 70 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 4 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 166 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 91 ISO 75-1/-2
DTUL @ 0.45 MPa 152 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 1.1 E-4/℃ ISO 11359-2
Elec Electrical properties Value Unit Test Standard
Volume resistivity 5 Ohm*m IEC 60093
Surface resistivity 1000 Ohm IEC 60093
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988-2 - Internal
 
Processing
Pre Drying
Predrying for conductive carbon based ESD grades is required.
 
Drying time (h):3
Drying temperature (℃):80 - 100