POM C 9021 AW 低摩擦,耐磨损

添加时间:2013-06-08  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
hostaform pom C 9021 AW
 
HOSTAFORM® C 9021 AW 14 BLACK
HOSTAFORM® C 9021 AW NATURAL
HOSTAFORM® C 9021 AW XAP2™ LS
HOSTAFORM® C 9021 AW XAP2™ LS 14
HOSTAFORM® C 9021 AW XAP2™ LS 14 BLACK
HOSTAFORM® C 9021 AW XAP2™ LS 22
HOSTAFORM® C 9021 AW XAP2™ LS 30/5084
HOSTAFORM® C 9021 AW XAP2™ LS10/5288
HOSTAFORM® C 9021 AW XAP2™ LS10/5356
HOSTAFORM® C 9021 AW XAP2™ LS10/5460
HOSTAFORM® C 9021 AW XAP2™ LS30/4502
HOSTAFORM® C 9021 AW XAP2™ LS60/5030
HOSTAFORM® C 9021 AW XAP2™ LS60/5487
HOSTAFORM® C 9021 XAP® AW 14 BLACK
HOSTAFORM® C 9021 XAP® AW 22
HOSTAFORM® C 9021 XAP® AWLS10/4306
HOSTAFORM® C 9021 XAP® AWLS10/5288
HOSTAFORM® C 9021 XAP® AWLS10/5356
HOSTAFORM® C 9021 XAP® AWLS10/5460
HOSTAFORM® C 9021 XAP® AWLS30/4502
 
HOSTAFORM C 9021 AW | POM | Tribological
 
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNS, 03-002
 
POM copolymer
 
Injection molding type like C 9021, with special additive modified; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; good wear properties and low coefficient of friction.
 
UL-registration in natural and black and a thickness more than 1.5 mm as UL 94 HB.
 
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
 
Ranges of applications: sliding parts for window lifter.
 
UL    = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
 
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
 
Melt temperature:190-230℃
Mould temperature:80-120℃
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1380 kg/m³ ISO 1183
Melt volume rate (MVR) 8 cm³/10min ISO 1133
MVR test temperature 190 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 2.1 % ISO 294-4
Mold shrinkage - normal 1.9 % ISO 294-4
Water absorption (23℃-sat) 0.65 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 2600 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 58 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 8 % ISO 527-2/1A
Nominal strain at break (50mm/min) 20 % ISO 527-2/1A
Tensile creep modulus (1h) 2300 MPa ISO 899-1
Tensile creep modulus (1000h) 1200 MPa ISO 899-1
Charpy impact strength @ 23℃ 150 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 130 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 6 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 5 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 166 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 88 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1.1 E-4/℃ ISO 11359-2
Flammability @1.6mm nom. thickn. HB class UL94
thickness tested (1.6) 1.5 mm UL94
UL recognition (1.6) UL - UL94
Flammability at thickness h HB class UL94
thickness tested (h) 3 mm UL94
UL recognition (h) UL - UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 100 Hz 3.8 - IEC 60250
Relative permittivity - 1 MHz 3.8 - IEC 60250
Dissipation factor - 100 Hz 20 E-4 IEC 60250
Dissipation factor - 1 MHz 50 E-4 IEC 60250
Volume resistivity 1E12 Ohm*m IEC 60093
Surface resistivity 1E14 Ohm IEC 60093
Electric strength 35 kV/mm IEC 60243-1
Comparative tracking index CTI 600 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988 - Internal
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
 
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
 
The product can then be stored in standard conditions until processed.
 
Drying time (h):3 - 4
Drying temperature (℃):100 - 120