POM C 52021 生产阶段快,抗溶解,高流动

添加时间:2013-06-07  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
hostaform pom C 52021
 
HOSTAFORM® C 52021 10/3772
HOSTAFORM® C 52021 14 BLACK
HOSTAFORM® C 52021 20/3552
HOSTAFORM® C 52021 20/4322
HOSTAFORM® C 52021 20/4361
HOSTAFORM® C 52021 20/5117
HOSTAFORM® C 52021 30/3912
HOSTAFORM® C 52021 30/5056
HOSTAFORM® C 52021 30/5061
HOSTAFORM® C 52021 39
HOSTAFORM® C 52021 60/3893
HOSTAFORM® C 52021 60/4117
HOSTAFORM® C 52021 60/4140
HOSTAFORM® C 52021 60/5002
HOSTAFORM® C 52021 80/3779
HOSTAFORM® C 52021 LS 30/6048
HOSTAFORM® C 52021 LS NATURAL
HOSTAFORM® C 52021 NATURAL
HOSTAFORM® C 52021 XAP® LS30/5473
HOSTAFORM® C 52021 XAP® LS30/5588
HOSTAFORM® C 52021 XAP® LS30/5615
HOSTAFORM® C 52021 XAP® LS60/5589
HOSTAFORM® C 52021 XAP® NATURAL
 
HOSTAFORM C 52021 | POM | Unfilled
 
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 06-002
 
POM copolymer
 
Extremly easy flowing Injection molding type for very thin-walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times; for mechanical lower requirements; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high esistance to thermal and oxidative degradation.
 
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, FDA compliant according to 21 CFR 177.2470
 
UL-registration in natural a thickness more than 0.81 mm, in black a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B for a thickness of 1.5 mm, electrical 105 ℃, mechanical 90℃
 
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
 
Ranges of applications: For very thin-walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times.
 
FDA   = Food and Drug Administration (USA)
BgVV  = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL    = Underwriters Laboratories (USA)
 
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
 
Melt temperature:190-230℃
Mould temperature:80-120℃
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1410 kg/m³ ISO 1183
Melt volume rate (MVR) 39 cm³/10min ISO 1133
MVR test temperature 190 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 1.9 % ISO 294-4
Mold shrinkage - normal 1.8 % ISO 294-4
Water absorption (23℃-sat) 0.65 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 3000 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 65 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 7 % ISO 527-2/1A
Nominal strain at break (50mm/min) 15 % ISO 527-2/1A
Tensile creep modulus (1h) 2500 MPa ISO 899-1
Tensile creep modulus (1000h) 1300 MPa ISO 899-1
Flexural modulus (23℃) 2800 MPa ISO 178
Charpy impact strength @ 23℃ 100 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 100 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 5 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 5 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 166 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 106 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1.1 E-4/℃ ISO 11359-2
Flammability @1.6mm nom. thickn. HB class UL94
thickness tested (1.6) 1.5 mm UL94
UL recognition (1.6) UL - UL94
Flammability at thickness h HB class UL94
thickness tested (h) 0.81 mm UL94
UL recognition (h) UL - UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 100 Hz 4 - IEC 60250
Relative permittivity - 1 MHz 4 - IEC 60250
Dissipation factor - 100 Hz 30 E-4 IEC 60250
Dissipation factor - 1 MHz 50 E-4 IEC 60250
Volume resistivity 1E12 Ohm*m IEC 60093
Surface resistivity 1E14 Ohm IEC 60093
Electric strength 35 kV/mm IEC 60243-1
Comparative tracking index CTI 600 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988 - Internal
Rheo Rheological Calculation properties Value Unit Test Standard
Density of melt 1200 kg/m³ Internal
Thermal conductivity of melt 0.19 W/(m K) Internal
Specific heat capacity of melt 2060 J/(kg K) Internal
Ejection temperature 163 Internal
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
 
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
 
The product can then be stored in standard conditions until processed.
 
Drying time (h):3 - 4
Drying temperature (℃):120 - 140