POM C 13031 抗溶解,耐碱,耐水解

添加时间:2013-06-05  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
hostaform pom C 13031
 
HOSTAFORM® C 13031 10/1570
HOSTAFORM® C 13031 10/2013
HOSTAFORM® C 13031 10/9022
HOSTAFORM® C 13031 10/9022 BLACK
HOSTAFORM® C 13031 11
HOSTAFORM® C 13031 14
HOSTAFORM® C 13031 14 BLACK
HOSTAFORM® C 13031 22
HOSTAFORM® C 13031 30/5693
HOSTAFORM® C 13031 30/5707
HOSTAFORM® C 13031 30/5905
HOSTAFORM® C 13031 33
HOSTAFORM® C 13031 70/5687 LIME GREEN
HOSTAFORM® C 13031 76
HOSTAFORM® C 13031 80/5453
HOSTAFORM® C 13031 80/5688 BLUE
HOSTAFORM® C 13031 87
HOSTAFORM® C 13031 90/5840
HOSTAFORM® C 13031 LS NATURAL
HOSTAFORM® C 13031 NATUR NATURAL
HOSTAFORM® C 13031 NATURAL
HOSTAFORM® C 13031 XAP® NATURAL
HOSTAFORM® C 2520 XAP® LS 40/4112
HOSTAFORM® C 2520 XAP® LS 40/5819
 
HOSTAFORM C 13031 | POM | Unfilled
 
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 04-002
 
POM copolymer
 
Easy flowing Injection molding type like C 13021, but with higher strength, rigidity and hardness over the entire permissible temperature range for HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
 
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, FDA compliant according to 21 CFR 177.2470
 
UL-registration for all colours and a thickness more than 1.5 mm as UL 94 HB; burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
 
Ranges of applications: For molded parts with higher requirements to strength, rigidity und hardness, ranges of applications with fuel contact.
 
FDA   = Food and Drug Administration (USA)
BgVV  = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
UL    = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
 
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
 
Melt temperature:190-230℃
Mould temperature:80-120℃
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1410 kg/m³ ISO 1183
Melt volume rate (MVR) 12 cm³/10min ISO 1133
MVR test temperature 190 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 2 % ISO 294-4
Mold shrinkage - normal 1.8 % ISO 294-4
Water absorption (23℃-sat) 0.65 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 3050 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 68 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 8 % ISO 527-2/1A
Nominal strain at break (50mm/min) 20 % ISO 527-2/1A
Tensile creep modulus (1h) 2750 MPa ISO 899-1
Tensile creep modulus (1000h) 1450 MPa ISO 899-1
Flexural modulus (23℃) 3000 MPa ISO 178
Charpy impact strength @ 23℃ 120 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 120 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 6.7 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 6 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 170 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 107 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1.1 E-4/℃ ISO 11359-2
Flammability @1.6mm nom. thickn. HB class UL94
thickness tested (1.6) 1.5 mm UL94
UL recognition (1.6) UL - UL94
Flammability at thickness h HB class UL94
thickness tested (h) 3 mm UL94
UL recognition (h) UL - UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 100 Hz 4 - IEC 60250
Relative permittivity - 1 MHz 4 - IEC 60250
Dissipation factor - 100 Hz 20 E-4 IEC 60250
Dissipation factor - 1 MHz 50 E-4 IEC 60250
Volume resistivity 1E12 Ohm*m IEC 60093
Surface resistivity 1E14 Ohm IEC 60093
Electric strength 35 kV/mm IEC 60243-1
Comparative tracking index CTI 600 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988 - Internal
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
 
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
 
The product can then be stored in standard conditions until processed.
 
Drying time (h):3 - 4
Drying temperature (℃):120 - 140