POM MC90 含矿物填料,抗撞击良好

添加时间:2013-06-04  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
泰科纳POM MC90
 
CELCON® MC90 CA44051 WHITE
CELCON® MC90 CD3501 BLACK
CELCON® MC90 CF3500 NATURAL
 
CELCON MC90 | POM | Mineral Reinforced
 
Description
Celcon® acetal copolymer grade MC90 is a mineral reinforced grade offering low warp, improved dimensional stability, improved stiffness, improved practical impact and retention of other base resin properties with good moldability.
 
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 03-002, M
 
Other Processing
Injection Molding
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the material.
 
Melt Temperature: Preferred range 182-199℃ (360-390℉). Melt temperature should never exceed 230℃ (450℉).
 
Mold Surface Temperature: Preferred range 82-93℃ (180-200℉) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120℃ (250℉) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65℃/150℉) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25℃ (80℉). In general, mold surface temperatures lower than 82℃ (180℉) may hinder weld line formation and produce a hazy surface or a surface with flow lines, pits and other included defects that can hinder part performance.
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1480 kg/m³ ISO 1183
Mold shrinkage - parallel 1.9 % ISO 294-4
Mold shrinkage - normal 1.6 % ISO 294-4
Water absorption (23℃-sat) 0.75 % ISO 62
Humidity absorption (23℃/50%RH) 0.2 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 3000 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 57 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 8 % ISO 527-2/1A
Flexural modulus (23℃) 2850 MPa ISO 178
Charpy notched impact strength @ 23℃ 6.8 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 5.5 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 6.3 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 165 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 97 ISO 75-1/-2
DTUL @ 0.45 MPa 152 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 1.2 E-4/℃ ISO 11359-2
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988-2 - Internal
 
Processing
Pre Drying
Drying time (h):3
Drying temperature (℃):80 - 100
 