POM GC20 含20%玻璃纤维增强

添加时间:2013-05-30  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
泰科纳POM GC20
 
CELCON® GC20 CD3501 BLACK
CELCON® GC20 CF3500 NATURAL
 
CELCON GC20 | POM | Glass Reinforced
 
Description
Celcon® GC20 is a glass coupled formulation containing 20% fiber glass reinforcement to improve strength and stiffness.
 
Chemical abbreviation according to ISO 1043-1: POM
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1540 kg/m³ ISO 1183
Water absorption (23℃-sat) 0.8 % ISO 62
Humidity absorption (23℃/50%RH) 0.2 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 7300 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 99 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.2 % ISO 527-2/1A
Flexural modulus (23℃) 7000 MPa ISO 178
Flexural strength (23℃) 130 MPa ISO 178
Charpy impact strength @ 23℃ 30 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 40 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 6 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 5.2 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 165 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 160 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 0.43 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 1.1 E-4/℃ ISO 11359-2
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988-2 - Internal
 
Processing
Pre Drying
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
 
Drying time (h):3
Drying temperature (℃):80 - 100