CELCON® CF802 CF3500 NATURAL
 
CELCON CF802 | POM | Specialty
 
Description
Celcon® acetal copolymer grade CF802 is a conductive, fuel compatible general purpose acetal copolymer. Celcon® CF802 has been developed to dissipate static electricity from fuel handling systems.
 
Please note Celcon® CF802 has special processing considerations to ensure static dissipation properties. Use minimum back pressure and slowest screw speed possible in retracting screw during cooling portion of cycle. Large gate size (>2 mm) recommended. Pneumatic conveying of material long distances is not recommended.
 
Other Processing
Injection Molding
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the material.
 
Melt Temperature: Preferred range 182-199℃ (360-390℉). Melt temperature should never exceed 230℃ (450℉).
 
Mold Surface Temperature: Preferred range 82-93℃ (180-200℉) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120℃ (250℉) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65℃/150℉) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25℃ (80℉). In general, mold surface temperatures lower than 82℃ (180℉) may hinder weld line formation and produce a hazy surface or a surface with flow lines, pits and other included defects that can hinder part performance.
 
ISO Data Mechanical properties Value Unit Test Standard
Phys Density 1470 kg/m³ ISO 1183
Mold shrinkage - parallel 1.7 % ISO 294-4
Mold shrinkage - normal 1.6 % ISO 294-4
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 3100 MPa ISO 527-2/1A
Tensile stress at yield (50mm/min) 60 MPa ISO 527-2/1A
Tensile strain at yield (50mm/min) 10 % ISO 527-2/1A
Tensile creep modulus (1h) 2130 MPa ISO 899-1
Tensile creep modulus (1000h) 1050 MPa ISO 899-1
Flexural modulus (23℃) 3100 MPa ISO 178
Charpy impact strength @ 23℃ 70 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 70 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 4.5 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 4.1 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 4.8 kJ/m² ISO 180/1A
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 167 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 100 ISO 75-1/-2
Coeff.of linear therm. expansion (parallel) 1 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 1.2 E-4/℃ ISO 11359-2
Elec Electrical properties Value Unit Test Standard
Volume resistivity 3 Ohm*m IEC 60093
Surface resistivity 2000 Ohm IEC 60093
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 9988-2 - Internal
 
Processing
Pre Drying
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
 
Drying time (h):3
Drying temperature (℃):80 - 100