LNP STAT-LOY POM KX95702

添加时间:2013-02-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

LNP™ STAT-LOY™ Compound POM KX95702

 

Also known as:LNP™ Stat-loy™ Compound PDX-K-95702 Product reorder name:KX95702
LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing Anti-Static. Added features of this material include: Antistat.

 

Property
TYPICAL PROPERTIES(1)

MECHANICAL Value Unit Standard
Tensile Stress,yield 410 kgf/cm² ASTM D 638
Tensile Stress,break 250 kgf/cm² ASTM D 638
Tensile Strain,yield 18.1 % ASTM D 638
Tensile Strain,break 75.5 % ASTM D 638
Tensile Modulus,50mm/min 15300 kgf/cm² ASTM D 638
Flexural Stress 470 kgf/cm² ASTM D 790
Flexural Modulus 14100 kgf/cm² ASTM D 790
Tensile Stress,yield 41 MPa ISO 527
Tensile Stress,break 31 MPa ISO 527
Tensile Strain,yield 14.6 % ISO 527
Tensile Strain,break 52.4 % ISO 527
Tensile Modulus,1mm/min 1110 MPa ISO 527
Flexural Stress 35 MPa ISO 178
Flexural Modulus 1350 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 16 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 230 cm-kgf ASTM D 3763
Multiaxial Impact 168 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 14 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 78 ASTM D 648
CTE,-40℃ to 40℃,flow 1.24E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 1.39E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.24E-04 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 1.39E-04 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 64 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.32 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 4.05 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1.7 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1.8 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 1.74 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 1.83 % ISO 294
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+09-1.E+11 Ohm ASTM D 257
Source GMD,last updated:2004/10/01
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Melt Temperature 195-205
Front-Zone 3 Temperature 200-210
Middle-Zone 2 Temperature 190-200
Rear-Zone 1 Temperature 175-190
Mold Temperature 70-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/10/01