Product Profile:
PLEXIGLAS® Resist zk20 is an amorphous thermoplastic molding compound that is slightly impact-modified (PMMA-I).
 
Typical properties of standard PLEXIGLAS® molding compounds are:
﹒excellent light transmission
﹒good mechanical properties.
 
Special properties of PLEXIGLAS® Resist zk20 are:
﹒increased break resistance to avoid demolding fractures during injection molding
﹒improved resistance to stress cracking
﹒AMECA listing.
 
Application:
Used for injection molding. Profile extrusion or coextrusion are also possible.
 
Examples:
lighting fixtures, writing and drawing utensils, domestic appliances and sanitaryware
 
含添加剂:冲击调节器
UL 黄卡2E65495-100986378
材料特点:高 ESCR(抗应力裂纹),高抗撞击
材料用途:电器用具,卫浴产品,文具,型材,医疗器械,照明装置
产品形式:颗粒料
加工方法:挤出,注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Resist zk20
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.17 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 2.00 cm³/10min ISO 1133
吸水率(平衡,23℃,50% RH) 0.30 % ISO 62
机械性能 额定值 单位制 测试方法
拉伸模量 2400 MPa ISO 527-2/1
拉伸应力(屈服) 62.0 MPa ISO 527-2/50
拉伸应变(屈服) 4.5 % ISO 527-2/50
断张率 22 % ISO 527-2
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 25 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 100 ISO 75-2/B
1.8 MPa,未退火 96.0 ISO 75-2/A
玻璃转化温度 112 ISO 11357-2
维卡软化温度 102 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.00010 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率2 91.0 % ISO 13468-2
注射 额定值 单位制
干燥温度 <90.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 230 到 240
模具温度 50.0 到 70.0