Product Profile:
PLEXIGLAS® Optical POQ62 is an amorphous thermoplastic molding compound based on polymethylmethacrylate (PMMA).
 
In addition to the familiar properties of PLEXIGLAS® molding compounds, such as
﹒excellent light transmission and brilliance,
﹒very good weather resistance,
﹒high mechanical strength, surface hardness and mar resistance,
 
PLEXIGLAS® Optical POQ62 is distinguished by its
﹒guaranteed purity and clarity,
﹒outstanding flow properties due to its low melt viscosity and its
﹒extremely accurate mold surface reproduction.
 
Application:
PLEXIGLAS® Optical POQ62 is particularly suitable for injection-compression molding and for injection-molding thin-walled parts with long flow paths. Further fields of application are two-component injection molding and special extrusion.
 
Examples:
Manufacture of moldings with microstructured surfaces and optical structures.
 
UL 黄卡2E65495-100986376
材料特点:High Hardness,Light Stabilized,高强度,流动性佳,耐气候影响,清晰度高
材料用途:光学应用
产品形式:颗粒料
加工方法:挤出,注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Optical POQ62
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.19 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 21.0 cm³/10min ISO 1133
吸水率(平衡,23℃,50% RH) 0.60 % ISO 62
机械性能 额定值 单位制 测试方法
拉伸模量 3300 MPa ISO 527-2/1
拉伸应力(断裂) 63.0 MPa ISO 527-2/5
拉伸应变(断裂) 2.8 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 20 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
维卡软化温度 97.0 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000080 cm/cm/℃ ISO 11359-2
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率3 92.0 % ISO 13468-2
雾度 <0.50 % ASTM D1003
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
注射 额定值 单位制
干燥温度 <80.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 260
模具温度 60.0 到 90.0