PMMA Hi-Gloss NTA-3 高光泽,高抗撞击,高流动

添加时间:2013-11-27  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Plexiglas PMMA Hi-Gloss NTA-3

Plexiglas® PMMA Hi-Gloss NTA-3
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Hi-Gloss NTA-3 is a compound with an increased heat deflection temperature based on polymethyl methacrylate (PMMA).
 
Besides the well-known properties of PLEXIGLAS® molding compound, such as
﹒good flow
﹒high mar resistance
﹒good weather resistance
﹒good polishability,
 
PLEXIGLAS® Hi-Gloss NTA-3 offers the added benefit of
﹒increased heat deflection temperature under load.
 
Application:
PLEXIGLAS® Hi-Gloss NTA-3 is particularly suitable for injection molding technical components.
Owing to its superior brilliance, high-gloss (Class A) surfaces can be obtained in opaque colors.
 
Examples:
automotive body parts: window channels, pillar panels
 
材料特点:高光泽,高抗撞击,流动性高,耐气候影响
材料用途:Automotive Backlights,Automotive Window Encapsulation,汽车防撞杆,汽车领域的应用,汽车外部零件,汽车外部装饰
产品外观:不透明
产品形式:颗粒料
加工方法:注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Hi-Gloss NTA-3
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.18 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 2.00 cm³/10min ISO 1133
吸水率(23℃,24 hr) >3.0 % ISO 62
机械性能 额定值 单位制 测试方法
拉伸模量 2900 MPa ISO 527-2/1
拉伸应力(断裂) 60.0 MPa ISO 527-2/5
拉伸应变(断裂) 2.6 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 16 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 106 ISO 75-2/B
1.8 MPa,未退火 106 ISO 75-2/A
玻璃转化温度 126 ISO 11357-2
维卡软化温度 116 ISO 306/B50
可燃性 额定值 单位制 测试方法
热灯丝点火温度 675 IEC 60695-2-13
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
注射 额定值 单位制
干燥温度 <100
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 250
模具温度 50.0 到 85.0