PMMA Heatstop 8N black 高光泽,耐磨蚀,耐气候

添加时间:2013-11-27  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Plexiglas PMMA Heatstop 8N black

Plexiglas® PMMA Heatstop 8N black
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Heatstop 8N black is an amorphous
thermoplastic molding compound (PMMA).
 
Typical properties of PLEXIGLAS® molding compounds are:
﹒good flow
﹒high mechanical strength, surface hardness and abrasion resistance
﹒very good weather resistance
 
Special properties of PLEXIGLAS® Heatstop 8N black are:
﹒heat-reflection (IR)
﹒high total solar reflection (TSR), reflects 21% of the solar energy
﹒reduces the heat build-up of plastic parts, thus increases the dimension stability.
 
Application:
PLEXIGLAS® Heatstop 8N black is suitable for injection molding of technical components, as well as for extrusion/coextrusion. Owing to its superior brilliance, high-gloss (Class A) black surfaces can be obtained.
 
Examples:
black automotive add-on parts like spoiler, pillar and roof trims, black automotive parts like roof modules.
 
材料特点:High Hardness,高强度,高光泽,流动性佳,耐磨蚀,耐气候影响
材料用途:汽车领域的应用,汽车外部零件,汽车外部装饰
产品外观:黑色
产品形式:颗粒料
加工方法:共挤出成型,挤出,注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Heatstop 8N black
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.19 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 3.00 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量 3300 MPa ISO 527-2/1
拉伸应力(断裂) 77.0 MPa ISO 527-2/5
拉伸应变(断裂) 5.5 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 20 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 103 ISO 75-2/B
1.8 MPa,未退火 98.0 ISO 75-2/A
玻璃转化温度 117 ISO 11357-2
维卡软化温度 108 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000080 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
注射 额定值 单位制
干燥温度 <98.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 260
模具温度 60.0 到 90.0