PMMA Heatresist hw55 高ESCR,高强度,共聚物

添加时间:2013-11-27  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Plexiglas PMMA Heatresist hw55

Plexiglas® PMMA Heatresist hw55
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Heatresist hw55 clear is a copolymer based on methyl methacrylate (MMA) with comonomer constituents.
 
Besides showing the familiar properties of standard PLEXIGLAS® molding compound, such as
﹒high light transmission,
﹒good flowability,
﹒high mechanical strength, surface hardness and abrasion resistance, as well as
﹒excellent weatherability,
 
PLEXIGLAS® Heatresist hw55 clear offers the additional benefits of
﹒increased heat deflection temperature under load and
﹒improved resistance to stress cacking
﹒optimised inherent color,
﹒AMECA listing.
 
Application:
PLEXIGLAS® Heatresist hw55 clear is particularly suitable for injection molding of technical items.
 
Examples:
lighted keys, luminaire covers, fiber optics.
 
UL 黄卡2E65495-247814
材料特点:High Hardness,高 ESCR(抗应力裂纹),高强度,共聚物,流动性佳,易着颜色,耐气候影响
材料用途:保护性遮盖物,光学应用,纤维
产品外观:清晰/透明
产品形式:颗粒料
加工方法:注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Heatresist hw55
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.19 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 1.20 cm³/10min ISO 1133
吸水率     ISO 62
23℃,24 hr 2.2 %
平衡,23℃,50% RH 0.60 %
机械性能 额定值 单位制 测试方法
拉伸模量 3600 MPa ISO 527-2/1
拉伸应力(断裂) 80.0 MPa ISO 527-2/5
拉伸应变(断裂) 3.5 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 20 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 109 ISO 75-2/B
1.8 MPa,未退火 106 ISO 75-2/A
玻璃转化温度 122 ISO 11357-2
维卡软化温度 119 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000070 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
光学性能 额定值 单位制 测试方法
折射率 1.510   ISO 489
透射率3 90.0 % ISO 13468-2
注射 额定值 单位制
干燥温度 <109
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 250
模具温度 60.0 到 90.0