Plexiglas PMMA 8H

Plexiglas® PMMA 8H
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® 8H is an amorphous thermoplastic molding compound (PMMA).
 
Typical properties of PLEXIGLAS® molding compounds are:
﹒good flow
﹒high mechanical strength, surface hardness and mar resistance
﹒high light transmission
﹒very good weather resistance
﹒free colorability due to crystal clarity.
 
Special properties of PLEXIGLAS® 8H molding compound are:
﹒optimum mechanical properties
﹒increased heat deflection temperature
﹒high melt strength
﹒AMECA listing.
 
Application:
Used for extruding optical and technical profiles and sheets.
 
Examples:
sheets, tubes, multi-skin sheets, coextrusion of window profiles and similar applications
 
Processing:
PLEXIGLAS® 8H can be processed on extruders with 3-zone general purpose screws for engineering thermoplastics.
 
Physical Form / Packaging:
PLEXIGLAS® molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags or in 500kg boxes with PE lining; other packaging on request.
 
UL黄卡2E65495-247805
材料特点:High Hardness,高 ESCR(抗应力裂纹),流动性良好,良好的熔体强度,易着颜色,耐气候影响
材料用途:管道,门窗,片材,型材
产品形式:颗粒料
加工方法:共挤出成型,挤出
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA 8H
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.19 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 0.800 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量 3300 MPa ISO 527-2/1
拉伸应力(断裂) 78.0 MPa ISO 527-2/5
拉伸应变(断裂) 6.5 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 20 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
维卡软化温度 108 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000080 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率3 92.0 % ISO 13468-2
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
挤出 额定值 单位制
干燥温度 <98.0
干燥时间 2.0 到 3.0 hr
熔体温度 220 到 260
模具温度 220 到 260