LNP STAT-LOY PMMA 93000LTH

添加时间:2013-02-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP™ STAT-LOY™ Compound PMMA 93000LTH
 
Also known as:LNP™ Stat-loy™ Compound 93000LTH Product reorder name:93000LTH
LNP* Stat-Loy* 93000LTH is a compound based on Acrylic resin featuring a permanent anti-static characteristic. Added features include: Transparent and Formulation Locked.
 
Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 400 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 7 % ASTM D 638
Tensile Modulus,5mm/min 18200 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 470 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 14900 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 68 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 66 ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity 1.15 - ASTM D 792
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+09-1.E+11 Ohm-cm ASTM D 257
Surface Resistivity 1.E+09-1.E+11 Ohm ASTM D 257
Static Decay,5000V to <50V <1 < seconds FTMS101B
Source GMD,last updated:2011/06/27
Parameter Injection Molding Value Unit
Drying Temperature 70-80
Drying Time 4 hrs
Maximum Moisture Content 0.05-0.1 %
Melt Temperature 200-210
Front-Zone 3 Temperature 205-215
Middle-Zone 2 Temperature 195-205
Rear-Zone 1 Temperature 180-195
Mold Temperature 10-50
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD, last updated:2011/06/27