添加时间:2013-05-28  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
泰科纳PBT
 
CELANEX® 5300-2 EF3022 NATURAL
CELANEX® 5300-2 EV4661 SIENNA BEIGE YR40
CELANEX® 5300-2 EY4662 TRUFFLE NH767L
 
CELANEX 5300-2 | PBT | Glass Reinforced
 
Description
Celanex 5300-2 is a 30% fiberglass reinforced polyester with improved surface finish. Celanex 5300-2 contains an internal lubricant.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1540 kg/m³ ISO 1183
Melt volume rate (MVR) 20 cm³/10min ISO 1133
MVR test temperature 265 ISO 1133
MVR test load 2.16 kg ISO 1133
Mold shrinkage - parallel 0.3-0.5 % ISO 294-4
Humidity absorption (23℃/50%RH) 0.2 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 10000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 135 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 3 % ISO 527-2/1A
Flexural modulus (23℃) 9000 MPa ISO 178
Flexural strength (23℃) 200 MPa ISO 178
Charpy impact strength @ 23℃ 49 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 48 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 9.5 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 9 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 8.3 kJ/m² ISO 180/1A
Rockwell hardness 93 M-Scale ISO 2039-2
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 225 ISO 11357-1,-2,-3
Glass transition temperature (10℃/min) 60 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 200 ISO 75-1/-2
DTUL @ 0.45 MPa 220 ISO 75-1/-2
DTUL @ 8.0 MPa 120 ISO 75-1/-2
Vicat softening temperature B50 (50℃/h 50N) 225 ISO 306
Coeff.of linear therm. expansion (parallel) 0.24 E-4/℃ ISO 11359-2
Coeff.of linear therm. expansion (normal) 0.75 E-4/℃ ISO 11359-2
Limiting oxygen index (LOI) 20 % ISO 4589
Flammability at thickness h HB class UL94
thickness tested (h) 0.71 mm UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 100 Hz 4.6 - IEC 60250
Relative permittivity - 1 MHz 4.2 - IEC 60250
Volume resistivity >1E13 Ohm*m IEC 60093
Surface resistivity >1E15 Ohm IEC 60093
Electric strength 30 kV/mm IEC 60243-1
Comparative tracking index CTI 350 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 7792-2 - Internal
Injection molding melt temperature 260 ISO 294
Injection molding mold temperature 82 ISO 294
Injection molding flow front velocity 300 mm/s ISO 294
Injection molding hold pressure 48 MPa ISO 294
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40℉ (-40℃) at 250℉ (121℃) for 4 hours.
 
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100℃.
 
Drying time (h):4
Drying temperature (℃):120 - 130