PBT 2302 GV1/15 含玻璃纤维15%增强

添加时间:2013-05-24  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
泰科纳PBT 2302 GV1/15
 
CELANEX® 2302 GV1/15 10/0242
CELANEX® 2302 GV1/15 10/0900
CELANEX® 2302 GV1/15 30/0566
CELANEX® 2302 GV1/15 30/2129
CELANEX® 2302 GV1/15 NATURAL
 
CELANEX 2302 GV1/15 | PBT | Glass Reinforced
 
Description
Chemical abbreviation according to ISO 1043-1: PBT Moulding compound ISO 7792- PBT/PET, MGHR, 08-060N, GF15
 
Polybutylene terephthalate, polymer blend, 15 % glass fibre reinforced, injection molded parts with superior gloss. Flammability UL 94 HB minimum thickness 0.85 mm. Recognition by Underwriters Laboratories, USA (UL)
 
Other Processing
Injection Molding
Melt Temperature                             265-275  ℃
Mold Temperature *)                           90-100  ℃
Maximum Barrel Residence Time **)               5-10  min
Injection Speed                                 fast
Peripheral screw speed                       max.0,3  m/sec
Back Pressure                                  10-30  bar
Injection Pressure                          600-1000  bar
Holding Pressure                             400-800  bar
Nozzle Design                  open design preferred
 
Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided.
 
Ticona recommends only externally heated hot runner systems.
 
*) For moulded parts with especially high requirements to the surface quality or dimensional stability, a mold temperature of up to 110℃ can be advantageous.
**) If the cylinder temperatures are higher than the recommended maximum temperatures, the max. residence time in the barrel has to be reduced.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1430 kg/m³ ISO 1183
Melt volume rate (MVR) 21 cm³/10min ISO 1133
MVR test temperature 265 ISO 1133
MVR test load 2.16 kg ISO 1133
Humidity absorption (23℃/50%RH) 0.15 % ISO 62
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 6100 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 110 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 3 % ISO 527-2/1A
Tensile creep modulus (1h) 5300 MPa ISO 899-1
Tensile creep modulus (1000h) 4300 MPa ISO 899-1
Flexural strength (23℃) 160 MPa ISO 178
Charpy impact strength @ 23℃ 35 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 35 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 6.5 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 6.5 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 255 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 190 ISO 75-1/-2
DTUL @ 8.0 MPa 65 ISO 75-1/-2
Vicat softening temperature B50 (50℃/h 50N) 210 ISO 306
Coeff.of linear therm. expansion (parallel) 0.35 E-4/℃ ISO 11359-2
Limiting oxygen index (LOI) 19 % ISO 4589
Flammability @1.6mm nom. thickn. HB class UL94
thickness tested (1.6) 1.4 mm UL94
UL recognition (1.6) UL - UL94
Flammability at thickness h HB class UL94
thickness tested (h) 0.85 mm UL94
UL recognition (h) UL - UL94
Elec Electrical properties Value Unit Test Standard
Relative permittivity - 100 Hz 4.1 - IEC 60250
Relative permittivity - 1 MHz 4 - IEC 60250
Dissipation factor - 100 Hz 12 E-4 IEC 60250
Dissipation factor - 1 MHz 180 E-4 IEC 60250
Volume resistivity >1E13 Ohm*m IEC 60093
Surface resistivity >1E15 Ohm IEC 60093
Electric strength 28 kV/mm IEC 60243-1
Comparative tracking index CTI 250 - IEC 60112
SpecProd Test specimen production Value Unit Test Standard
Processing conditions acc. ISO 7792 - Internal
Injection molding melt temperature 270 ISO 294
Injection molding mold temperature 90 ISO 294
Injection molding flow front velocity 200 mm/s ISO 294
Injection molding hold pressure 70 MPa ISO 294
Rheo Rheological Calculation properties Value Unit Test Standard
Density of melt 1220 kg/m³ Internal
Thermal conductivity of melt 0.15 W/(m K) Internal
Specific heat capacity of melt 1820 J/(kg K) Internal
Ejection temperature 218 Internal
 
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
 
CELANEX should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
 
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100℃.
 
Drying time (h):2-4
Drying temperature (℃):120 - 140