PA66 R533H 含33%玻纤增强,热稳定,润滑

添加时间:2013-06-17  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
Vydyne PA66 R533H
 
Vydyne® R533H
聚酰胺66
玻璃纤维33%增强材料
Ascend Performance Materials LLC.
 
产品说明
The Vydyne R533® Series of 33% glass fiber reinforced nylons are available in natural,black and heat stabilized versions. They are general purpose,injection molding grades which are lubricated for good machine feed,flow and mold release.
 
Vydyne R533 Series resins are members of a wide range of glass reinforced resins supplied by Ascend Performance Materials. Other glass fiber loadings available include 13% and 43%.
 
Vydyne R533 Series resins have tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs,energy consumption,and part weight are key advantages of Vydyne glass reinforced Nylon 6,6 resins over aluminum and/or zinc die cast parts.
 
Vydyne R533H is a heat stabilized grade,formulated to minimize the oxidative and thermal degradation of the nylon polymer when exposed to elevated temperatures for extended periods of time. Vydyne R533H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275℉ and short-term peak temperatures as high as 475℉.
 
含添加剂:热稳定剂、润滑剂
填料增强:含33%玻璃纤维增强
材料特点:刚性高、高强度、经润滑、良好的流动性、热稳定性、脱模性能良好
材料用途:齿轮、动力/其它工具、汽车的发动机罩下的零件
ul 档案号:E70062
材料外观:黑色、自然色
产品牌号:PA66 R533H
湘樟版权:http://www.simibc.com/sujiao/pa66/vydyne/r533h.html
产品形式:颗粒料
加工方法:注射成型
 
物料数据
物理性能 干燥 调节后的 单位制 测试方法
密度 1.4 -- g/cm3 ISO 1183
收缩率       ISO 294-4
横向流量:23℃,2.00 mm 0.9 -- %
流量:23℃,2.00 mm 0.4 -- %
吸水率       ISO 62
23℃,24 hr 0.8 -- %
平衡,23℃,50% RH 1.8 -- %
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量(23℃) 10200 7900 MPa ISO 527-2
拉伸应力(断裂,23℃) 205 148 MPa ISO 527-2
拉伸应变(断裂,23℃) 3 5 % ISO 527-2
弯曲模量(23℃) 9700 6500 MPa ISO 178
弯曲强度(23℃) 290 205 MPa ISO 178
泊松比 0.4 --   ISO 527-2
冲击性能 干燥 调节后的 单位制 测试方法
简支梁缺口冲击强度       ISO 179
-30℃ 12 -- kJ/m2
23℃ 12 -- kJ/m2
简支梁缺口冲击强度       ISO 179
-30℃ 75 -- kJ/m2
23℃ 85 -- kJ/m2
悬壁梁缺口冲击强度(23℃) 12 -- kJ/m2 ISO 180
热性能 干燥 调节后的 单位制 测试方法
热变形温度        
0.45 MPa,未退火 260 -- ISO 75-2/B
1.8 MPa,未退火 250 -- ISO 75-2/A
维卡软化温度 252 -- ISO 306/B
溶融温度(DSC) 260 -- ISO 3146
线形膨胀系数       ISO 11359-2
流动:23 到 55℃,2.00 mm 2.1E-5 -- cm/cm/℃
横向:23 到 55℃,2.00 mm 1.1E-4 -- cm/cm/℃
RTI Elec       UL 746
0.750 mm 140 --
1.50 mm 140 --
3.00 mm 140 --
RTI Imp       UL 746
0.750 mm 125 --
1.50 mm 125 --
3.00 mm 125 --
RTI Str       UL 746
0.750 mm 140 --
1.50 mm 140 --
3.00 mm 140 --
电气性能 干燥 调节后的 单位制 测试方法
体积电阻率(3.00 mm) 3.0E+15 -- ohm·cm IEC 60093
耐电强度2(23℃,3.00 mm) 16 -- kV/mm IEC 60243-1
耐电弧性(3.00 mm) PLC 6 --   ASTM D495
相比耐漏电起痕指数(CTI)(3.00 mm) PLC 2 --   UL 746
漏电起痕指数(3.00 mm) 400 到 599 -- V IEC 60112
高电弧燃烧指数(HAI)       UL 746
0.750 mm PLC 0 --  
1.50 mm PLC 0 --  
3.00 mm PLC 0 --  
高电压电弧起痕速率(HVTR)(3.00 mm) PLC 1 --   UL 746
热丝引燃(HWI)       UL 746
0.750 mm PLC 4 --  
1.50 mm PLC 3 --  
3.00 mm PLC 4 --  
可燃性 干燥 调节后的 单位制 测试方法
UL 阻燃等级       UL 94
0.750 mm,All colors HB --  
1.50 mm,All colors HB --  
3.00 mm,All colors HB --  
极限氧指数 28 -- % ASTM D2863
注射 干燥 单位制
干燥温度 < 70.0
干燥时间 1.0 到 3.0 hr
建议注入量 40 到 80 %
建议的最大回制料比例 25 %
螺筒后部温度 280 到 310
螺筒中部温度 280 到 310
螺筒前部温度 280 到 310
射嘴温度 280 到 310
加工(熔体)温度 285 到 305
模具温度 65.0 到 95.0
注塑温度 55.0 到 140 MPa
注射速度 快速  
保压 55.0 到 140 MPa
背压 0.200 到 1.00 MPa
螺杆转速 60 到 120 rpm
合模力 2.7 到 6.2 kN/cm2
垫层 3.00 到 6.40 mm