PA66 47 冲击改性纯尼龙树脂

添加时间:2013-03-28  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
Vydyne
Vydyne® PA66 47
PA66
聚酰胺66
Ascend Performance Materials Operations LLC
 
产品说明:
Vydyne 47 is a general-purpose, impact-modified PA66 resin. Available in natural, Vydyne 47 is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 47 is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.
 
Typical Applications/End Uses:
Vydyne 47 may be used in most market segments, including industrial, consumer, automotive and electrical applications. Typical end uses include clips, fasteners, gears, cable ties, electrical connectors and many other parts that require additional toughness at room and low temperatures.
 
黄卡下载:E70062-100757496
含添加剂:冲击改性剂
材料特性:冲击改性,抗溶剂,高抗撞击,易加工,耐磨损,耐低温冲击,耐化学,耐汽油,耐油,韧性良好,通用
材料用途:齿轮,电气/电子应用领域,工业应用,紧固件,连接器,汽车领域的应用,消费品应用领域
加工方法:注射成型
产品外观:自然色粒子
杜邦销售:苏州希普能工程塑料 185 5121 3137 谭经理
塑料牌号:PA66 47
版权所有:http://www.simibc.com/sujiao/pa66/vydyne/47.html
 
产品物性:
物理性能 干燥 调节后的 单位制 测试方法
密度 1.10 -- g/cm³ ISO 1183
收缩率       ISO 294-4
垂直流动方向:23℃,2.00 mm 1.6 -- %
流动方向:23℃,2.00 mm 1.8 -- %
吸水率       ISO 62
23℃,24 hr 1.2 -- %
平衡,23℃,50% RH 2.3 -- %
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量(23℃) 2780 1740 MPa ISO 527-2
拉伸应力       ISO 527-2
屈服,23℃ 60.0 45.0 MPa
断裂,23℃ 52.0 40.0 MPa
拉伸应变(断裂,23℃) 22 60 % ISO 527-2
弯曲模量(23℃) 2300 780 MPa ISO 178
弯曲应力(23℃) 70.0 24.0 MPa ISO 178
冲击性能 干燥 调节后的 单位制 测试方法
简支梁缺口冲击强度       ISO 179
-40℃ 11 18 kJ/m²
-30℃ 17 24 kJ/m²
23℃ 19 62 kJ/m²
简支梁无缺口冲击强度       ISO 179
-30℃ 无断裂 无断裂  
23℃ 无断裂 无断裂  
悬壁梁缺口冲击强度       ISO 180
-40℃ 12 18 kJ/m²
-30℃ 16 24 kJ/m²
23℃ 18 44 kJ/m²
热性能 干燥 调节后的 单位制 测试方法
热变形温度        
0.45 MPa,未退火 185 -- ISO 75-2/B
1.8 MPa,未退火 63.0 -- ISO 75-2/A
熔融温度 260 -- ISO 11357-3
线形热膨胀系数       ISO 11359-2
流动:23 到 55℃,2.00 mm 1.1E-4 -- cm/cm/℃
横向:23 到 55℃,2.00 mm 1.4E-4 -- cm/cm/℃
RTI Elec       UL 746
0.750 mm 125 --
1.50 mm 125 --
3.00 mm 125 --
RTI Imp       UL 746
0.750 mm 75.0 --
1.50 mm 75.0 --
3.00 mm 75.0 --
RTI       UL 746
0.750 mm 85.0 --
1.50 mm 85.0 --
3.00 mm 85.0 --
电气性能 干燥 调节后的 单位制 测试方法
体积电阻率(0.750 mm) 1.0E+12 -- ohm·cm IEC 60093
介电强度(1.00 mm) 24 -- kV/mm IEC 60243
耐电弧性 PLC 5 --   ASTM D495
漏电起痕指数(3.00 mm) 600 -- V IEC 60112
高电弧燃烧指数(HAI)       UL 746
0.750 mm PLC 0 --  
1.50 mm PLC 0 --  
3.00 mm PLC 0 --  
高电压电弧起痕速率 (HVTR) PLC 1 --   UL 746
热丝引燃 (HWI)       UL 746
0.750 mm PLC 4 --  
1.50 mm PLC 4 --  
3.00 mm PLC 2 --  
可燃性 干燥 调节后的 单位制 测试方法
UL 阻燃等级       UL 94
0.750 mm HB --  
1.50 mm HB --  
3.00 mm HB --  
灼热丝易燃指数       IEC 60695-2-12
0.750 mm 750 --
1.50 mm 775 --
3.00 mm 725 --
热灯丝点火温度       IEC 60695-2-13
0.750 mm 775 --
1.50 mm 800 --
3.00 mm 750 --
注射 干燥 单位制
干燥温度 80.0
干燥时间 4.0 hr
建议的最大回制料比例 25 %
料筒后部温度 280 到 310
料筒中部温度 280 到 310
料筒前部温度 280 到 310
射嘴温度 280 到 310
加工(熔体)温度 285 到 305
模具温度 65.0 到 95.0
苏州希普能塑料代理销售原包首诺PA66材料,由于价格时常浮动网上就不一一报价,还请电话咨询价格,谢谢关照!