CELSTRAN® PA66-SF6-02 AF3005 NATURAL

 

CELSTRAN PA66-SF6-02 | PA66 | Stainless Steel Reinforced

 

Description
6% stainless steel reinforced nylon 6/6

 

Other Processing
Injection Molding
Celstran can be processed on a standard injection molding unit. A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.

 

Melt Temp:290-300℃.
Mold Temp:75-85℃.

 

ISO Data Physical properties Value Unit Test Standard
Phys Density 1190 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 3600 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 80 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 3.2 % ISO 527-2/1A
Flexural modulus (23℃) 3200 MPa ISO 178
Flexural strength (23℃) 130 MPa ISO 178
Charpy notched impact strength @ 23℃ 3.8 kJ/m² ISO 179/1eA

 

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4
Drying temperature (℃):70-80