CELSTRAN PA66-GF60-02-US | PA66 | Glass Reinforced

 

Description
60% long glass fiber reinforced, heat stabilized, Nylon 6/6

 

Other Processing
Injection Molding
Celstran can be processed on a standard injection molding unit. A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.

 

Melt Temp:310-315℃.
Mold Temp:90-100℃.

 

ISO Data Physical properties Value Unit Test Standard
Phys Density 1690 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 21600 MPa ISO 527-2/1A
Tensile modulus (80℃) 11900 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 280 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.7 % ISO 527-2/1A
Elongation at break (80℃) 2 % ISO 527-2/1A
Flexural modulus (23℃) 19400 MPa ISO 178
Flexural strength (23℃) 460 MPa ISO 178
Charpy notched impact strength @ 23℃ 54 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
DTUL @ 1.8 MPa 263 ISO 75-1/-2

 

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4
Drying temperature (℃):70-80