CELSTRAN® PA66-GF50-07 AC3033 GRAY
CELSTRAN® PA66-GF50-07 AD3002 BLACK
CELSTRAN® PA66-GF50-07 AF3001 NATURAL

 

CELSTRAN PA66-GF50-07 | PA66 | Glass Reinforced

 

Description
50% long fiber glass reinforced, enhanced flow, Nylon 6/6

 

ISO Data Physical properties Value Unit Test Standard
Phys Density 1560 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 16600 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 230 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.8 % ISO 527-2/1A
Flexural modulus (23℃) 15000 MPa ISO 178
Flexural strength (23℃) 360 MPa ISO 178
Charpy notched impact strength @ 23℃ 33 kJ/m² ISO 179/1eA

 

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4
Drying temperature (℃):70-80