Celstran PA66 GF50-02 AD3007

添加时间:2013-05-01  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

CELSTRAN PA66-GF50-02 AD3007 | PA66 | Glass Reinforced

 

Description

Material code according to ISO 1043-1: PA66

 

Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.

 

Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.

 

The very isotropic shrinkage in the molded parts minimizes the warpage.

 

Complex parts can be manufactured with high reproducibility by injection molding.

 

Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.


ISO Data Physical properties Value Unit Test Standard
Phys Density 1570 kg/m³ ISO 1183
Mech Mechanical properties Value Unit Test Standard
Tensile modulus (1mm/min) 13600 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 205 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.8 % ISO 527-2/1A
Charpy impact strength @ 23℃ 60 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 23 kJ/m² ISO 179/1eA
Therm Thermal properties Value Unit Test Standard
Melting temperature (10℃/min) 260 ISO 11357-1,-2,-3

 

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%

 

Drying time (h):2-4
Drying temperature (℃):70-80