Celstran PA66 GF40-07

添加时间:2013-05-01  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

CELSTRAN PA66-GF40-07 | PA66 | Glass Reinforced

 

Description
40% long fiber glass reinforced, enhanced flow, Nylon 6/6


ISO Data Physical properties Value Unit Test Standard
Phys Density 1450 kg/m³ ISO 1183
Mech Tensile modulus (1mm/min) 13000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 205 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2 % ISO 527-2/1A
Flexural modulus (23℃) 12100 MPa ISO 178
Flexural strength (23℃) 320 MPa ISO 178
Charpy notched impact strength @ 23℃ 23 kJ/m² ISO 179/1eA

 

Processing
Pre Drying

 

Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4
Drying temperature (℃):70-80