Celstran PA66 GF40-02P11/15

添加时间:2013-04-30  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

CELSTRAN® PA66-GF40-02 AD3002 BLACK P11/
CELSTRAN® PA66-GF40-02 P11/15
CS PA66-GF40-02 P11/15 C0

 

CELSTRAN PA66-GF40-02P11/15 | PA66 | Glass Reinforced

 

Description
Material code according to ISO 1043-1: PA66

 

Heat stabilized Nylon 66 reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.

 

Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.

 

The very isotropic shrinkage in the molded parts minimizes the warpage.

 

Complex parts can be manufactured with high reproducibility by injection molding.

 

Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.

 


Other Processing
Injection Molding
During the processing of CELSTRAN it is important to watch and control melt shear, for excessive shear reduces fiber length and mechanical performance as well.

 

Processing recommendation:
- Conventional 3 zone screw, screw diameter minimum 40 mm
- Design flow channels for low melt shear
- Back pressure and screw rotation to realize a continous plastification performance and thus a homogeneous melt.
- Apply higher temperature settings than for short fiber compounds

 

Melt temperature (in the screw anteroom):300-315℃
Mold surface temperature:90-120℃


ISO Data Physical properties Value Unit Test Standard
Phys Density 1460 kg/m³ ISO 1183
Mech Tensile modulus (1mm/min) 13700 MPa ISO 527-2/1A
Tensile modulus (80℃) 9000 MPa ISO 527-2/1A
Tensile strength (80℃) 130 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 180 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.5 % ISO 527-2/1A
Elongation at break (80℃) 2 % ISO 527-2/1A
Flexural modulus (23℃) 12600 MPa ISO 178
Flexural modulus (80℃) 8000 MPa ISO 178
Flexural strength (23℃) 260 MPa ISO 178
Flexural strength (80℃) 250 MPa ISO 178
Charpy impact strength @ 23℃ 40 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 41 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 23 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 23 kJ/m² ISO 179/1eA
Notched impact strength (Izod) @ 23℃ 24 kJ/m² ISO 180/1A
Notched impact strength (Izod) @-30℃ 35 kJ/m² ISO 180/1A
Therm Melting temperature (10℃/min) 261 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 255 ISO 75-1/-2
DTUL @ 8.0 MPa 240 ISO 75-1/-2

 

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Drying time (h):2-4
Drying temperature (℃):70-80