Celstran PA66 GF40-02-US

添加时间:2013-05-01  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

CELSTRAN® PA66-GF40-02 AD3002 BLACK
CELSTRAN® PA66-GF40-02 AD3002 BLACK 25MM
CELSTRAN® PA66-GF40-02 AD3004 BLACK
CELSTRAN® PA66-GF40-02 AF3001 NATURAL
CELSTRAN® PA66-GF40-02 AF3001 NATURAL P1

 

CELSTRAN PA66-GF40-02-US | PA66 | Glass Reinforced

 

Description
40% Long glass fiber reinforced, heat stabilized, Nylon 6/6

 

Other Processing
Injection Molding
Celstran can be processed on a standard injection molding unit. A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.

 

Melt Temp:295-300℃.
Mold Temp:85-95℃.


ISO Data Physical properties Value Unit Test Standard
Phys Density 1450 kg/m³ ISO 1183
Mech Tensile modulus (1mm/min) 13300 MPa ISO 527-2/1A
Tensile modulus (80℃) 7500 MPa ISO 527-2/1A
Tensile strength (80℃) 120 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 215 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2 % ISO 527-2/1A
Elongation at break (80℃) 2.9 % ISO 527-2/1A
Flexural modulus (23℃) 13500 MPa ISO 178
Flexural modulus (80℃) 6800 MPa ISO 178
Flexural strength (23℃) 355 MPa ISO 178
Flexural strength (80℃) 210 MPa ISO 178
Charpy impact strength @ 23℃ 95 kJ/m² ISO 179/1eU
Charpy impact strength @ -30℃ 46 kJ/m² ISO 179/1eU
Charpy notched impact strength @ 23℃ 35 kJ/m² ISO 179/1eA
Charpy notched impact strength @ -30℃ 26 kJ/m² ISO 179/1eA
Unnotched impact str (Izod) @ 23℃ 47 kJ/m² ISO 180/1U
Unnotched impact str (Izod) @-30℃ 43 kJ/m² ISO 180/1U
Therm Melting temperature (10℃/min) 261 ISO 11357-1,-2,-3
DTUL @ 1.8 MPa 255 ISO 75-1/-2
DTUL @ 8.0 MPa 240 ISO 75-1/-2
SpecProd Test specimen production Value Unit Test Standard
Injection molding melt temperature 305 ISO 294
Injection molding mold temperature 90 ISO 294
Injection molding flow front velocity 80 mm/s ISO 294
Injection molding hold pressure 83 MPa ISO 294

 

Processing
Pre Drying

 

Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4
Drying temperature (℃):70-80