CELSTRAN PA66-GF30-02 | PA66 | Glass Reinforced

 

Description
30% long glass fiber reinforced, heat stabilized, Nylon 6/6

 


Other Processing
Injection Molding
Celstran can be processed on a standard injection molding unit. A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.

 

Melt Temp:290-295℃.
Mold Temp:85-95℃.


ISO Data Physical properties Value Unit Test Standard
Phys Density 1360 kg/m³ ISO 1183
Mech Tensile modulus (1mm/min) 9700 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 170 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.1 % ISO 527-2/1A
Flexural modulus (23℃) 9000 MPa ISO 178
Flexural strength (23℃) 280 MPa ISO 178
Charpy notched impact strength @ 23℃ 23 kJ/m² ISO 179/1eA
Therm DTUL @ 1.8 MPa 252 ISO 75-1/-2

 

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4
Drying temperature (℃):70-80